Silica Mortar

Main Composition: SiO2≥92%
Application: Industrial Furnaces
Raw Material: Silica Sand
Color: Yellow
Bonding Time : 1~3 min
Refractoriness Under Load 0.2Mpa: ≥1500℃
Capacity: 3000 MT per month
Package: Export Wooden Pallets and Paper Bags
Introduction:
Silica mortar is also known as joint filler. It is made of silica powder and by a ratio of SiO2 powder. The binder is normally made of clay or additive.
 
Features:
1.High adhesive strength.
2.High refractoriness.
3.Superior installation performance.
 
Application:
Silica mortar is mainly used for laying and repair of coke oven, hot blast stove, glass furnace and other masonry of high quality silica bricks industrial furnace.
 
Technical Data:
Item Silica Mortar
RGN-94 JGN-92 BGN-96 GGN-94
SiO2 (%) ≥94 ≥92 ≥96 ≥94
Cold Rupture Bonding Strength
After Drying 110℃ (Mpa)                                                            
1.0 1.0 0.8 0.5
Cold Rupture Bonding Strength
After Firing 1400℃*3h (Mpa)            
3.0 3.0 0.5 1.5
Refractoriness Under Load (0.2MPa)             1600 1500 1620 --
Grain Composition +0.5mm (%) ≤1.0 ≤3.0 ≤2.0 ≤3.0
Grain Composition -0.074mm (%) 60 50 60 50
Bonding Time (min) 1-2 1-2 2-3 1-2
CN/ Refractoriness(Cone) 170 166 172 170
 
 
 