High Temperature Binder

Product Introduction：
High temperature binder is prepared by adding refractory powder into inorganic or organic binders. Based on the material of refractory bricks, refractory powder with similar physical and chemical properties to refractory bricks is selected to meet the requirements of different refractory bricks.

Product Highlights:
-High bond strength of bonder
-High high-temperature binding power
-Pollution-free on environment
 
 
Application:
High temperature binder are mainly used for the masonry of refractory products.
GX-2 High-temperature binder is used for the bond between refractory brick and refractory fiber, refactory fiber and metal in industrial furnace below1200℃.
GX-3 High-temperature binder is used for the bond between refractory materials below 1500℃.

Technical Data:
 

Main performance
Item	Type	KL-03	KL-04	KL-05
State		Liquid, thickness	Liquid, thickness	Liquid, thickness
Operating temperature(℃)		1350	1350	1500
Proportion(g/cm)		1.44~1.84	1.20~1.25	1.9
PH		1.4~2.0	8.5~10.0	8.0~9.0
Dynamic viscosity(CP)		1.40~1.60	5.0~8.0
Tensile Strength(MPa)		7.50	8.15	2.94

 
 

Name                                 Properties		High-temperature bonder
		GX-2	GX-3
Max Service Temperature（℃）		1200	1500
Dosage（Kg/m²）		1.8~3.6	2.0~3.5
Consistency（MM）		210	195
Flexural Bond Strength（Mpa）	105℃	4.5	4.0
	1100℃	8.9	8.1
	1300℃	9.1	10.2
	1400℃		11.5
Linearchange after Heating（%）		-1.2	-1.0

 
 

Properties Band		YDM series Binder	High Aluminum Binder	Clay Binder	Acidproof Binder
Max Service Temperature（℃）		1500	1400	1250	900
Dosage（Kg/m²）		4.5-5.5	4.5~5.5	5-6.5	5-5.5
Consistency（MM）		160	170	180	160
Flexural Bond Strength（Mpa）	110℃×24h	2	2	2	650℃×3h ≥20
	815℃×3h	4	4	4
Linear Changes on Reheating	℃×3h	1400	1400	1200	650
	%	-0.3	-0.3	-0.5	±0.5
Granularity(%)	110℃×24h	3	4	5	8
	815℃×3h	40	40	40	40
Al2O3≥%		65	55	40	SiO₂ ≥70%
Acid resistance（≥%）					95